Experimental investigation of binder based on rice husk ash and eggshell lime on soil stabilization under acidic attack

Scientific Reports volume 12, Article number: 7542 (2022) Cite this article

2439 Accesses

3 Citations

1 Altmetric

Metrics details

This study evaluates the use of rice husk ash (RHA)-eggshell lime (ESL) and RHA-commercial lime (CL) as alternative binders for clayey soil stabilization, as well as the performance of soil-binder mixtures under acidic attack. A central composite design was carried out to analyze the reactivity by batch tests with a sulfuric acid solution. Physical and mechanical behavior was evaluated by compaction test and unconfined compressive strength (UCS). Reactivity tests demonstrated better neutralization of contaminant acidity for mixtures with ESL. The highest compressive strength, reactivity and partial encapsulation of toxic elements are associated with application of 30% RHA and 6% ESL in the soil. A C–S–H gel is observed in poorly crystalline phases through the XRD pattern. The application of RHA-ESL in soils exposed to acidic attack has environmental feasibility. Analysis of RHA grinding processes combined with the mixture strength over time, and its application tests in impermeable barriers, in landfills, are recommended.

Solid waste represents a growing concern at the global level, mainly due to population growth and consumerism1. A major waste generator is the world’s production of rice, estimated to produce 750 million tons of rice husk yearly2. Furthermore, there is a new field of studies related to the valuation of waste from the food sector, the eggshell. The world generates 4.91 million tons of eggshell waste annually, being 278,250 tons in Brazil3.

Rice processing generates 160 million tons of waste composed of rice husk, which is destined to landfills2 or for energy purposes4. The portion of rice husk used for energy purposes is regularly used as fuel in boilers for energy production, and after burning, it generates a new waste: rice husk ash (RHA). RHA is considered a pozzolana due to its source of amorphous silica4; which promotes the application of RHA in multiple destinations, such as production of concrete5,6,7, mortars8,9, soil remediation processes10, adsorption11; constitution of geopolymers12, and effluent treatment13.

The characteristics of RHA and its potential as a pozzolanic material strongly depend on the methods and conditions that originated the RHA4,14. RHA from different industries may have different amorphous silica content and specific surface areas, as well as other distinct characteristics that are still poorly explored14,15. Therefore, not only the characterization of RHA is important, but also the exploration of its use in mixtures with materials that increase the alkalinity of the environment (e.g. lime).

In this context, many studies have evaluated the use of eggshell waste as an alternative calcium source for different geotechnical and civil construction applications3,16,17,18,19,20. Furthermore, studies observed that eggshell lime (ESL) presents itself as an excellent material for soil stabilization along with a pozzolanic source, such as RHA, and a more sustainable binder than dolomitic lime because it avoids limestone mineral extraction and improvement4,20,21.

Although these studies explore the isolated application of RHA and eggshell lime for the development of new materials, there is a lack of studies using these two materials in a mixture to improve the mechanical and reactive behavior of compacted clayey residual soils. These mixtures can be applied to waterproofing barriers in landfills, for example, and subject to contact with acidic contaminants from the disposal of waste or tailings. These barriers can prevent degradation in its microstructure and prevent the migration of contaminants to the subsoil22.

This paper fills this gap by comparing RHA-eggshell lime with RHA-commercial lime as alternative binders for soil stabilization. An experimental design was performed to investigate factors that could significantly influence the reactivity of clayey soil-RHA-lime mixtures. In addition, characterization of rice husk ash, unconfined compressive strength test, environmental performance, chemical and mineralogical analyses were conducted in mixtures.

Figure 1 presents the materials and methods used in this study, including: materials characterization; tests to determine the composition of the alternative binder; and physical–mechanical, environmental, chemical and mineralogical analysis of soil-binder mixtures.

Study methodology flowchart.

Materials used were residual basalt soil, rice husk ash (RHA), eggshell lime (ESL), and hydrated commercial lime (CL). The residual basalt soil used was collected in the experimental area of the Federal University of Fronteira Sul, Brazil. The RHA comes from a thermoelectric plant located in the state of Rio Grande do Sul, Brazil, that burns the rice husk at a temperature of 800–1000 °C for 8–12 s, and then slowly cooling to room temperature. The RHA was used without any prior processing.

Eggshell lime (ESL) was produced in laboratory23. First, the eggshells were washed with distilled water and subjected to a drying process in an oven at a temperature of 105 °C for 24 h, and then they were ground in a knife mill and calcined at a temperature of 1200 °C for 6 h. For comparison purposes, a hydrated commercial lime (dolomitic lime) was used because it is frequently applied for soil improvement in Brazil4.

The RHA was collected at the thermoelectric plant and prepared according to the Brazilian standard NBR 1000724. The parameters of moisture content and pH were determined according to Brazil25. The physical characterization of the material was performed by testing the specific gravity of the sample, following D854 standard26. The determination of the specific surface area of the RHA was performed by analyzing Brunauer, Emmett and Teller—BET isotherms, using nitrogen. In addition, the size of the particles was characterized both through laser, using the laser diffraction equipment and particle analyzer, model Cilas-1064.

The RHA was further chemically characterized by X-ray fluorescence spectrophotometry (XRF) analysis, using a Malvern Panalytical® X-ray fluorescence spectrometer, Zetium model with STD-1 (Standardless) calibration. The samples were pressed for analysis, performed with patterns of chemical elements between fluorine and uranium. The quantification of the organic matter content in the RHA was carried out employing a quali-quantitative determination of the material's loss on ignition. The firing conditions were at a temperature of 1020 °C for 2 h, with detection of 0.1% and normalization at 100%.

The mineralogical composition of rice husk ash was analyzed through X-ray diffraction (XRD) analysis by the powder method. The analysis was performed using a copper tube with voltage parameters of 45–40 kV/mA, angular variation of 2°–70°, with a step of 0.02° every 300 s. The pozzolanicity of RHA was qualitatively evaluated, according to the Fratini chemical test, according to the European standard27 and mineralogical composition.

To study the morphology and microstructure of the particles, the samples were analyzed using scanning electron microscopy (SEM), Tescan brand equipment, model Vega 3. The following analytical conditions were used in the analyses: backscattered electrons (BSE) with magnification of 40, 150, 500, and 3000 times, electron beam of voltage of 10 kV.

Additionally, the RHA was characterized as to leaching and solubilization of contaminants for environmental classification, according to Brazilian standards NBR 1000428, NBR 1000529, and NBR 1000630. The extracts had their chemical composition analyzed and compared with the limits imposed in Annex F for leachate and Annex G for solubilized, both present in NBR 1000428.

The soil under study was characterized in terms of its particle size distribution, according to31, as well as for the test of specific unit weight of grains26.

Table 1 presents physical properties of RHA. The RHA is composed of low humidity and alkaline pH (9.50).

As noted, the RHA has a low specific unit weight of grains (Table 1) when compared to the soil used (2.58 g/cm3). Kumar and Gupta32 observed a similar specific unit weight of grains of the RHA, with a value of 1.98 g/cm3. The incorporation of RHA in the soil leads to a decrease in its density, as observed by Qu et al.33. However, based on the results, rice husk ash can increase soil quality, in terms of stability and resistance.

XRF results (Table 2) show that RHA consists of high silica oxide content (87.6%), and small percentages of potassium (2.87%), calcium (0.88%), iron (0.61%) and magnesium (0.33%) oxides. These oxides are important in pozzolanic materials, and which may vary depending on the combustion process4.

According to the Fratini method27 test result, RHA is a pozzolana with low reactivity, classified a class “N” pozzolana. This result is in agreement with the literature, e.g. RHA applied as a pozzolanic material in cement mixtures7. The RHA mineralogical composition (Fig. 2) is essentially cristobalite (SiO2) and quartz (SiO2), being considered a material with crystalline and amorphous phases.

RHA mineralogical composition.

In terms of microstructure, Fig. 3 illustrates the morphology and microstructure of the RHA, using scanning electron microscopy (SEM) analysis. In addition, the presence of corn cob-shaped particles is verified (Fig. 3B), related to the organization of residue molecules in the backbone structure.

RHA morphology at ×40 (a), ×150 (b), ×500 (c) and ×3000 (d) magnification.

Leaching results (Table 3) show that the RHA does not present toxicity as no chemical element of the leached extract exceeded the limits established by Brazilian legislation (Annex F)28. However, the RHA presented solubilization of manganese, fluoride, and phenol compounds at concentrations higher than those indicated in Annex G28 (Table 4). Therefore, the RHA is classified as Class II A-Non-Hazardous Non-inert (e.g. it may present biodegradability, combustibility, or water-solubility properties)28. The concentration of solubilized manganese is justified by the significant presence of the element in the chemical composition of the RHA (0.36% MnO). Rice husks have phenolic acids in their composition34, which possibly explains the phenol solubilized in the RHA studied. Due to the rice husk35 and rice husk ash36,37 are efficient adsorbent materials for water defluoridation, it is believed that fluoride solubilized in the RHA comes from the adsorption of the element during the rice husk processing.

The hydrated ESL presents 72.90% of calcium oxide and minerals in the form of portlandite (Ca(OH)2), calcite (CaCO3), and magnesium peroxide (MgO2)21. The CL is in its majority composed of 45.9% CaO and 23.6% MgO; constituted by portlandite, calcite, and magnesium-based minerals3. Additional information regarding hydrated ESL and CL properties can be found in Consoli et al.21 and Araújo et al.3, respectively.

The mineralogical composition of residual basalt soil consists of quartz (SiO2), hematite (Fe2O3), kaolinite (Al2(Si2O5)(OH)4) and anatase (TiO2)38. Geotechnical properties indicates a clayey silty soil according to grain size distribution31, with liquid limit (%) of 56, plastic limit (%) of 50 and plastic index (%) of 439, and MH classification40, with high compressibility and medium plasticity.

The reactive behavior, referring to the incorporation of RHA in a mixture with residual clayey soil and ESL or CL, was studied through batch tests. The determination of the RHA and both limes levels to be incorporated into the soil was carried out employing a central composite factorial experimental design, with the addition of face-centered axial points to investigate the non-linearity of the behavior, if necessary. The measured variable was the difference between the final and initial pH of the contaminating solution, and the control variables were initial pH (2 and 6), RHA content (2% and 40%) and lime content (2% and 10%). The experiments were conducted in 2 blocks for each lime. Table 4 presents factors and levels of experimental design.

The total content of RHA was limited to 40% to investigate the effects of carbonation of free lime in the results of strength and reactive behavior41. The pH range was adopted because soil changes under the effect of inorganic acidic attack, usually occur between pH ranges of 3–642. Considering high acidity events, the literature recommends studying lower pH values, such as close to 122,38,43. Batch tests were performed following standard D 4646-0344. The mass/solution ratio used at each experimental point was 1:20. The samples were shaken on an orbital shaker table, under 150 rpm, at a constant temperature of approximately 25 °C for a period of 24 h, to simulate an acidic attack on the mixtures. The response variable (reactivity) was calculated through the initial pH variation and after contact with the acidic solution.

Based on preliminary results from the reactive behavior evaluation tests, 30% ash (in relation to the soil weight) was adopted to maximize the use of the waste in soil stabilization.

The ICL—initial consumption of lime test was used to determine the minimum lime content for pozzolanic reactions to occur in the ash-soil mixture. This method allows the evaluation of the lime increment ratio until the pH stabilization of the solution, which is composed of soil, ash, and distilled water45.

The particle size distribution of the mixtures and soil was performed using sieving and sedimentation31. Compaction tests were carried out for two mixtures, one with ESL (Mixture 1) and another with CL (Mixture 2) and a soil sample without ash or lime increment. The samples were prepared and compaction following the Brazilian standard46,47, adopting the normal Proctor energy.

The mechanical behavior of Mixtures 1 and 2 was evaluated using unconfined compression strength tests (UCS). The specimens were tested in a hydraulic press, according to the Brazilian standard48 after the curing time. The curing times studied were 7, 14, and 28 days, and the process took place in a humid chamber with a constant temperature of 23 ± 2 °C. Table 5 presents the soil- RHA-lime mixtures composition.

The mixture with the best physical–mechanical and reactive performance was subjected to chemical and mineralogical characterization, after being subjected to rupture with 28 days of curing. The concentrations of chemical elements and the mineralogical composition of the mixtures were determined by the XRF and XRD techniques, respectively. The environmental performance of the best-performing mixture was also evaluated by analyzing the acidic contaminant (sulfuric acidic solution, pH 4) after contact with the mixture in a batch test, according to an adaptation of the D4646-03 standard44. After 24 h of testing, the sample was filtered and the chemical composition of the extract was analyzed by inductively coupled plasm atomic emission spectrometry (ICP-AES), and later compared with49, which provides information about limits and standards for soil quality and Annex G of NBR 1000428.

Figure 4 shows the distribution and particle size of mixtures 1 and 2, the soil, and RHA. The mixtures of the two materials with lime allowed the modification for a material with well-distributed particles of silt, clay, and sand, with similar behavior for the studied CL and ESL. Regarding the particle size distribution of the RHA, the material has an average diameter of 45 µm, with a uniform particle size distribution.

Particle size distribution of mixtures, compared to soil and RHA.

Figures 5 and 6 present the relationships of factors and response variables combined for Mixtures 1 and 2, using contour surfaces obtained after statistical analysis and modeling of the behavior of the response variables. After statistical analysis of variance with 95% significance, the variables that most significantly influenced UCS were the pH and the % CL and % ESL, followed by the % RHA, being only non-linear behavior was observed for pH in mixture 2.

Contour surface of the experimental design of Mixture 1.

Contour surface of the experimental design of Mixture 2.

For both mixtures, lower ash contents result in the best reactivities, also higher lime contents, and the most acidic pH range. The addition of lime to the soil is responsible for increasing the alkalinity of the mixtures and stabilizing it, through the combination and exchange of calcium ions50, which explains the directly proportional relationship between the increase in lime addition content and pH elevation.

The combination of CL contents from 4 to 8% with higher ash contents present reactivity of 150–200%. These results, when applied to leachates with a pH range of 3.5–4.5, corresponding to a pH elevation of 5–9, respectively. According to CONAMA 43051, effluents with a pH in the range of 5–9 can be released into water bodies without risk. Thus, the contact of the acidic contaminant with the soil mixture results in the reduction of environmental liabilities due to the percolation of high acidity leachates into groundwater and surface waters.

Mixture 1 with ESL showed a better ability to neutralize the contaminant's acidity, resulting in greater reactivity. These results show a significant reduction in the use of lime, as only 6% of ESL corresponds to higher reactivities than mixtures with 8% CL. This can be explained by the fact that eggshell lime has higher concentrations of calcium, reaching more than 72.90% of calcium oxide available for reaction, while CL has 43.56% CaO.

The physico-mechanical behavior of the mixtures was evaluated with 6% lime (ESL or CL) (obtained using the ICL method)45 and 30% RHA, based on the reactivity results obtained previously. Figure 7 presents the soil compaction curves and the mixtures under study. The incorporation of RHA significantly increases soil moisture, previously with a maximum dry specific weight of 14.5 kN/m3 and an optimal moisture content of 30%. The mixtures with the addition of CL and ESL behaved similarly, however, the mixtures with ESL had lower densities and higher humidity when compared to the mixtures with the addition of CL.

Compaction curves for Mixture 1 (ESL), Mixture 2 (CL), and soil.

The addition of RHA to the soil significantly affects the parameters of moisture content and dry unit weight (γd), being beneficial for fine-grained soils, as it presents an improvement of behavior of soil without compaction, decreasing the dry specific weight and increasing the optimum moisture content. The specimens submitted to the UCS test were cast under the conditions presented with maximum dry specific weight and optimum moisture content, being 12.5 kN/m3 and 36.1% for the mixture with commercial lime (CL), and 12.1 kN/m3 and 39.1% for the mixture with eggshell lime (ESL).

Figure 8 shows the unconfined compression tests of both mixtures for curing times of 7, 14, and 28 days. Mixture 1 shows greater strength than Mixture 2 due to high calcium oxide content (72.9%) from ESL available for pozzolanic reactions. The mixtures with 28 days of curing did not give high strengths, stabilizing after 14 days (Fig. 8). However, the results obtained allow the mixtures application, with the minimum strength being 200 kPa (e.g. impermeable barriers of landfills)52, allowing the application of mixtures with ESL with 14 days of curing (226 kPa).

Unconfined compression strength at 7, 14, and 28 days of curing the mixtures.

The UCS results are explained by the crystalline silica predominance compared to the amount of amorphous silica in the RHA. Furthermore, RHA has a substantial concentration of silica oxide and low aluminum, which decreases the formation of aluminosilicates, reducing the mixture's strength53. RHA mixtures pre-treated by grinding can produce better results, the smaller particles fill the voids and help the formation of a denser and stronger specimen. Despite this, RHA was used in natural conditions, allowing it to be applied without pretreatment costs.

Table 6 presents the environmental performance results of Mixture 1. It is possible to notice that only two chemical elements were detected in the acidic contaminant extract: aluminum (Al) and sodium (Na). Bearing in mind that the origin of these elements is the crude RHA, as they are the elements present in higher concentrations in the solubilized extract of the RHA. The limits of national and international water quality standards CONAMA 46049, Dutch list54, EPA55 and NBR 10004-Annex G28 were not exceeded for both metals in the Mixture 1.

The addition of eggshell lime in the soil provides a reduction in toxicity, contributing to the inertization of RHA in the mixture. This was also observed by Soares, Quina and Quinta-Ferreira56, who studied the incorporation of ESL in soil, and observed the immobilization of heavy metals such as lead (Pb) and zinc (Zn), with acidic conditions favorable to Zn retention, as also observed in the present study with the acidic attack under pH 4.

XRF results (Table 7) show that Mixture 1 is composed mainly of silica (40.3%), iron (21.9%), aluminum (18.0%), and calcium oxides originated from the raw materials used in the mixture, i.e., clayey soil, RHA and ESL, respectively.

The XRD (Fig. 9) indicates the presence of kaolinite (Al2(Si2O5)(OH)4), quartz (SiO2), cristobalite (SiO2), tobermorite (Ca5Si6O16(OH)2·4H2O) and hematite (Fe2O3). Kaolinite, hematite, quartz and cristobalite originated from the soil and the RHA, respectively. The mineral tobermorite, which resembles the structure of hydrated calcium silicate gel (C–S–H), was observed in poorly crystalline phases. Also, portlandite (the main constituent of ESL) was not identified in the diffractogram, indicating that this mineral was consumed on the pozzolanic reactions.

Mineralogical composition of the Mixture 1 after 28 days of cure time.

Based on the findings of this study, the following conclusions were drawn:

The incorporation of the RHA-ESL binder to a clayey residual soil allowed a satisfactory mixture for the improvement of the mechanical and reactive behavior, promoting the partial encapsulation of metals present in the rice husk ash;

30% RHA in the soil with 6% ESL represented the mixture with the best reactive behavior for the neutralization of acidic contaminants in the soil, as it raised the pH and prevented the solubilization of toxic elements;

The addition of ESL presented satisfactory environmental performance considering the applicable regulations;

ESL showed to be a more efficient binder than CL in terms of mechanical strength and reactivity;

XRF results show that the soil-RHA-ESL mixture is composed majorly by silica (40.3%), iron (21.9%) and aluminum (18.0%) oxides;

XRD of soil-RHA-ESL mixture indicates the presence of kaolinite, quartz, cristobalite, tobermorite and hematite. A C–S–H gel is observed in poorly crystalline phases through the XRD pattern;

Because of the maximum UCS achieved after 14 and 28 curing days, an engineering application of the soil-RHA-ESL mixture could be foreseen in impermeable barriers of landfills.

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

D’amato, A. D., Mancinelli, S. & Zoli, M. Complementarity vs substitutability in management behaviors. Ecol. Econ. 123, 84–94. https://doi.org/10.1016/j.ecolecon.2015.12.005 (2016).

Article Google Scholar

Mosaberpanah, M. A. & Umar, S. A. Utilizing rice husk ash as supplement to cementitious materials on performance of ultra high performance concrete—a review. Mater. Today Sustain. https://doi.org/10.1016/j.mtsust.2019.100030 (2020).

Article Google Scholar

De Araújo, M. T., Ferrazzo, S. T., Bruschi, G. J. & Consoli, N. C. Mechanical and environmental performance of eggshell lime for expansive soils improvement. Transport. Geotech. 31, 100681. https://doi.org/10.1016/j.trgeo.2021.100681 (2021).

Article Google Scholar

Moayedi, H., Aghel, B., Abdullahi, M. M., Nguyen, H. & Rashid, A. S. A. Applications of rice husk ash as green and sustainable biomass. J. Clean. Prod. 237, 117851. https://doi.org/10.1016/j.jclepro.2019.117851o (2019).

Article CAS Google Scholar

Rattanachu, P., Toolkasikorn, P., Tangchirapat, W., Chindaprasirt, P. & Jaturapitakkul, C. Performance of recycled aggregate concrete with rice husk ash. Cement Concr. Compos. 108, 103533. https://doi.org/10.1016/j.cemconcomp.2020.103533 (2020).

Article CAS Google Scholar

Rumman, R., Bari, M. S., Manzur, T., Kamal, M. R. & Noor, M. A. A durable concrete mix design approach using combined aggregate gradation bands and rice husk ash based blended cement. J. Build. Eng. 30, 101303. https://doi.org/10.1016/j.jobe.2020.101303 (2020).

Article Google Scholar

Miller, S. A., Cunningham, P. R. & Harvey, J. T. Rice-based ash in concrete: A review of past work and potential environmental sustainability. Resour. Conserv. Recycl. 146, 416–430. https://doi.org/10.1016/j.resconrec.2019.03.041 (2019).

Article Google Scholar

Torres-Carrasco, M. et al. Critical aspects in the handling of reactive silica in cementitious materials: Effectiveness of rice husk ash vs nano-silica in mortar dosage. Construct. Build. Mater. 223, 360–367. https://doi.org/10.1016/j.conbuildmat.2019.07.023 (2019).

Article CAS Google Scholar

Font, A. et al. Design and properties of 100% waste-based ternary alkali-activated mortars: Blast furnace slag, olive-stone biomass ash and rice husk ash. J. Clean. Prod. 243, 118568. https://doi.org/10.1016/j.jclepro.2019.118568 (2020).

Article CAS Google Scholar

Kiran, B. R. & Prasad, M. N. V. Biochar and rice husk ash assisted phytoremediation potentials of Ricinus communis L. for lead-spiked soils. Ecotoxicol. Enviro. Saf. 183(15), 109574. https://doi.org/10.1016/j.ecoenv.2019.109574 (2019).

Article CAS Google Scholar

Song, J. U., Lee, J. S. & Yoon, H. K. Application of electrical conductivity method for adsorption of lead ions by rice husk ash. J. Int. Meas. Confed. 144, 126–134. https://doi.org/10.1016/j.measurement.2019.04.094 (2019).

Article Google Scholar

Wen, N., Zhao, Y., Yu, Z. & Liu, M. A sludge and modified rice husk ash-based geopolymer: Synthesis and characterization analysis. J. Clean. Prod. 226, 805–814. https://doi.org/10.1016/j.jclepro.2019.04.045 (2019).

Article CAS Google Scholar

Huzir, N. M. et al. Optimization of coagulation-flocculation process for the palm oil mill effluent treatment by using rice husk ash. Ind. Crops Prod. 139, 111482. https://doi.org/10.1016/j.indcrop.2019.111482 (2019).

Article CAS Google Scholar

Rêgo, J. H. S., Nepomuceno, A. A., Figueiredo, E. P. & Hasparyk, N. P. Microstructure of cement pastes with residual rice husk ash of low amorphous silica content. Constr. Build. Mater. 80, 56–68. https://doi.org/10.1016/j.conbuildmat.2014.12.059 (2015).

Article Google Scholar

Bie, R., Song, X., Liu, Q., Ji, X. & Chen, P. Cement and concrete composites studies on effects of burning conditions and rice husk ash (RHA) blending amount on the mechanical behavior of cement. Cement Concr. Compos. 55, 162–168. https://doi.org/10.1016/j.cemconcomp.2014.09.008 (2015).

Article CAS Google Scholar

Jijo, J., Kasinathan, P. P. & Snowline, S. A. Egg shell ash as auxiliary addendum to lime stabilization of an expansive soil. J. Solid Waste Technol. Manage. 11, 15–25. https://doi.org/10.5276/JSWTM.2017.15 (2017).

Article Google Scholar

James, J., Priya, K. J., Karthkika, P., Kokila, P. & Vidyasgar, V. Valorisation of egg shell ash as a potential replacement for lime in stabilization of expansive soils. Build. Mater. Struct. 63, 13–20. https://doi.org/10.5937/GRMK2003013J (2020).

Article Google Scholar

Hasan, M. et al. Effect of optimum utilization of silica fume and eggshell ash to the engineering properties of expansive soil. J. Mater. Res. Technol. 14, 1401–1418. https://doi.org/10.1016/j.jmrt.2021.07.023 (2019).

Article CAS Google Scholar

Poorveekan, K., Ath, K. M. S., Anburuvel, A. & Sathiparan, N. Investigation of the engineering properties of cementless stabilized earth blocks with alkali-activated eggshell and rice husk ash as a binder. Constr. Build. Mater. 277, 122371. https://doi.org/10.1016/j.conbuildmat.2021.122371 (2021).

Article CAS Google Scholar

Saldanha, R. B., da Rocha, C. G., Caicedo, A. M. L. & Consoli, N. C. Technical and environmental performance of eggshell lime for soil stabilization. Constr. Build. Mater. 298, 123648. https://doi.org/10.1016/j.conbuildmat.2021.123648 (2021).

Article Google Scholar

Consoli, N. C., Caicedo, A. M. L., Saldanha, R. B., Filho, H. C. S. & Acosta, C. J. M. Eggshell produced limes: Innovative materials for soil stabilization. J. Mater. Civ. Eng. 32, 11. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003418 (2020).

Article Google Scholar

Knop, A., VanGulck, J., Heineck, K. S. & Consoli, N. C. Compacted artificially cemented soil-acid leachate contaminant interactions: Breakthrough curves and transport parameters. J. Hazard Mater. 155(1–2), 269–276. https://doi.org/10.1016/j.jhazmat.2007.11.056 (2008).

Article CAS PubMed Google Scholar

Ngoya, T., Aransiola, E. F. & Oyekola, O. Optimisation of biodisel production from waste vegetable oil and eggshell ash. S. Afr. J. Chem. Eng. 23(1), 145–156. https://doi.org/10.1016/j.sajce.2017.05.003 (2017).

Article Google Scholar

ABNT NBR 10007. Sampling of solid waste. (ABNT, 2004a). https://www.abnt.org.br.

MAPA, BRAZIL. Manual de métodos analíticos oficiais para fertilizantes e corretivos. (Brasília, 2017). https://www.gov.br/agricultura.

ASTM D854. Standard Test Methods for Specific Gravity of Soil Solids by Water Pycnometer. (ASTM International, 2014). https://www.astm.org.

IPQ-Instituto português da qualidade 2011-NP EN 196-5: 2011. Methods of testing cement-Part 5: Pozzolanicity test for pozzolanic cement. Lisboa (2011).

ABNT NBR 10004. Solid waste-Classification. https://www.abnt.org.br. (2004).

ABNT NBR 10005. Procedure for obtention leaching extract of solid wastes. https://www.abnt.org.br (2004).

ABNT 10006. Procedure for obtention of solubilized extraction of solid wastes. https://www.abnt.org.br (2004).

ASTM D7928. Standard test method for particle-size distribution (gradation) of fine-grained soils using the sedimentation (hydrometer) analysis. https://www.astm.org (2017).

Kumar, A. & Gupta, D. Behavior of cement-stabilized fiber-reinforced pond ash, rice husk ash-soil mixtures. Geotext. Geomembr. 44, 466–474. https://doi.org/10.1016/j.geotexmem.2015.07.010 (2016).

Article MathSciNet Google Scholar

Qu, J., Li, B., Wei, T., Li, C. & Liu, B. Effects of rice-husk ash on soil consistency and compactibility. CATENA 122, 54–60. https://doi.org/10.1016/j.catena.2014.05.016 (2014).

Article CAS Google Scholar

Butsat, S. & Siriamornpun, S. Antioxidant capacities and phenolic compounds of the husk, bran and endosperm of Thai rice. Food Chem. 119, 606–613. https://doi.org/10.1016/j.foodchem.2009.07.001 (2010).

Article CAS Google Scholar

Gebrewold, B. D., Kijjanapanich, P., Rene, E. R., Lens, P. N. L. & Annachhatre, A. P. Fluoride removal from groundwater using chemically modified rice husk and corn cob activated carbon. Environ. Technol. (United Kingdom) 40, 2913–2927. https://doi.org/10.1080/09593330.2018.1459871 (2019).

Article CAS Google Scholar

Goswami, R. & Kumar, M. Removal of fluoride from aqueous solution using nanoscale rice husk biochar. Groundw. Sustain. Dev. 7, 446–451. https://doi.org/10.1016/j.gsd.2017.12.010 (2018).

Article Google Scholar

Vivek Vardhan, C. M. & Srimurali, M. Utilization of rice husk ash for defluoridation of water. In Recent Trends in Waste Water Treatment and Water Resource Management (eds Ghosh, S. et al.) (Springer, 2020). https://doi.org/10.1007/978-981-15-0706-9_21.

Chapter Google Scholar

Ferrazzo, S. T. et al. Effects of acidic attack on chemical, mineralogical, and morphological properties of geomaterials. Environ. Sci. Pollut. Res. 27, 37718–37732. https://doi.org/10.1007/s11356-020-09834-6 (2020).

Article CAS Google Scholar

ASTM D4318. Standard test methods for liquid limit, plastic limit, and plasticity index of soils. https://www.astm.org (2017).

ASTM D2487. Standard Classification of Soils for Engineering Purposes. https://www.astm.org (2017).

Koteng, D. O. & Chen, C. Strength development of lime–pozzolana pastes with silica fume and fly ash. Constr. Build. Mater. 84, 294–300. https://doi.org/10.1016/j.conbuildmat.2015.03.052 (2015).

Article Google Scholar

Chavali, R. V. P., Reddy, P. H. P., Murthy, V. R. & Sivapullaiah, P. V. Swelling characteristics of soils subjected to acid contamination, soils and foundations. Jpn. Geotech. Soc. 58(1), 110–121. https://doi.org/10.1016/j.sandf.2017.11.005 (2018).

Article Google Scholar

Liu, Y., Gates, W. P. & Bouazza, A. Acid induced degradation of the bentonite component used in geosynthetic clay liners. Geotext Geomembr. 36, 71–80. https://doi.org/10.1016/j.geotexmem.2012.10.011 (2013).

Article CAS Google Scholar

ASTM D4646-03. Standard test method for 24-h batch-type measurement of contaminant sorption by. https://www.astm.org (2008).

Consoli, N. C., Saldanha, R. B. & Scheuermann, H. C. Short- and long-term effects of sodium chloride on strength and durability of coal fly ash stabilized with carbide lime. Can. Geotech. J. 56, 12. https://doi.org/10.1139/cgj-2018-0696 (2019).

Article CAS Google Scholar

ABNT NBR 6457. Soil samples—preparation for compactation and characterization tests. https://www.abnt.org.br (2016).

ABNT NBR 7182. Soil—compaction test. https://www.abnt.org.br (2020).

ABNT NBR 12025. Soil-cement—simple compression test of cylindrical specimens—method of test. https://www.abnt.org.br (2012).

CONAMA Resolução 460. Altera a Resolução no 420, de 28 de dezembro de 2009, do Conselho Nacional do Meio Ambiente-CONAMA, que dispõe sobre critérios e valores orientadores de qualidade do solo quanto à presença de substâncias químicas e dá outras providências. (Official Diary of the Union, Brasilia). http://conama.mma.gov.br (2013).

Ferreira, R. C., Faleiro, H. T. & Freire, W. J. Desempenho físico-mecânico de solo argiloso estabilizado com cal e silicato de sódio visando aplicação em construções rurais. Pesquisa Agropecuária Trop. 35(3), 191–198 (2005).

Google Scholar

CONAMA Resolução 430. Dispõe sobre as condições e padrões de lançamento de efluentes, complementa e altera a Resolução no 357, de 17 de março de 2005, do Conselho Nacional do Meio Ambiente (Official Diary of the Union, Brasilia). http://conama.mma.gov.br (2011).

Lukiantchuki, J. A. & Esquivel, E. R. Hydraulic conductivity and shear strength behavior of compacted lateritic soil-bentonite mixtures used for sanitary landfill liners. Soils Rocks 33, 69–79 (2010).

Google Scholar

Nazari, A., Bagheri, A. & Riahi, S. Properties of geopolymer with seeded fly ash and rice husk bark ash. Mater. Sci. Eng. A 528(24), 7395–7401. https://doi.org/10.1016/j.msea.2011.06.027 (2011).

Article CAS Google Scholar

VROM—Spatial Planning and the Environment. Dutch target and intervention values. Ministerie van Volksuisveting Ruimteli-jke Ordening en Milieubeheer. p 51. https://www.esdat.net/environmental%20standards/dutch/annexs_i2000dutch%20environmental%20standards.pdf (2020).

USEPA. Ground water and drinking water: National primary drinking water regulations. Accessed April 05, 2022. https://www.epa.gov/ground-water-and-drinking-water/national-primary-drinking-water-regulations#Inorganic (2021).

Soares, M. A. R., Quina, M. J. & Quinta-Ferreira, R. M. Immobilisation of lead and zinc in contaminated soil using compost derived from industrial eggshell. J. Environ. Manage. 164, 137–145. https://doi.org/10.1016/j.jenvman.2015.08.042 (2015).

Article CAS PubMed Google Scholar

Download references

The authors wish to explicit their appreciation to MCT-CNPq (Edital Produtividade em Pesquisa) and PRO-ICT UFFS (Project 2020-0454) for the support to the research group.

Environmental and Sanitary Engineering, Universidade Federal da Fronteira Sul - Campus Erechim, Erechim, RS, 99700-970, Brazil

Joice Batista Reis, William Mateus Kubiaki Levandoski & Jonas Duarte Mota

Graduate Program in Environmental Science and Technology, Universidade Federal da Fronteira Sul - Campus Erechim, Erechim, RS, 99700-970, Brazil

Giovana Pelisser & Eduardo Pavan Korf

Graduate Program in Civil Engineering, Universidade Federal do Rio Grande do Sul, Porto Alegre, RS, 90035-190, Brazil

Suéllen Tonatto Ferrazzo

College of Engineering and Architecture, Universidade de Passo Fundo, Passo Fundo, RS, 99052-900, Brazil

Adriana Augustin Silveira

You can also search for this author in PubMed Google Scholar

All authors contributed to the study conception and design. Material preparation, data collection and analysis were performed by J.B.R., W.M.K.L. and J.D.M. The first draft of the manuscript was written by J.B.R., G.P., S.T.F. and all authors commented on previous versions of the manuscript. All authors read and approved the final manuscript. In addition, A.A.S. and E.P.K. were also responsible for the supervision.

Correspondence to Eduardo Pavan Korf.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Reis, J.B., Pelisser, G., Levandoski, W.M.K. et al. Experimental investigation of binder based on rice husk ash and eggshell lime on soil stabilization under acidic attack. Sci Rep 12, 7542 (2022). https://doi.org/10.1038/s41598-022-11529-6

Download citation

Received: 08 March 2022

Accepted: 22 April 2022

Published: 09 May 2022

DOI: https://doi.org/10.1038/s41598-022-11529-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Environmental Science and Pollution Research (2023)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.